论文编号:CL058  论文字数:8538,页数:20

 摘 要：本文首先设计并建造了不锈钢反应釜。在此基础上，进行超高分子量羟基硅油及氨基硅油的合成及优化，并最终确定两者的筛选及配合比例，制备羊毛特滑硅油。研究结果表明：脱水时间为2hr，催化剂用量0.01%，温度控制在160℃。采用进口D4，可获得满意的超高分子量羟基硅油，将该硅油与氨基硅油相配合，并织物处理可知：超高分子量羟基硅油与氨基硅油2：1比例复配，分子量大的氨基硅油与分子量小的氨基硅油按1：1比例复配，可获得较佳的综合平滑、柔软、蓬松的效果。
关键词：特种平滑硅油；超高分子量羟基硅油；氨基硅油

Abstract: The first design and construction of a stainless steel reactor. On this basis, for ultra-high molecular weight hydroxy-silicone oil and the synthesis and optimization, and ultimately determine both the selection and to meet proportion of wool special slippery silicone oil. The results show that: dehydration time for 2 hr, the amount of catalyst 0.01 percent, temperature control in the 160 ℃. Imported D4, will be satisfied with the ultra-high molecular weight hydroxy silicone oil, the oil and oil-fit and fabric processing know: ultra-high molecular weight hydroxy silicone oil and oil-ratio of 2:1 compound, a molecular weight The oil-and small-molecular-weight oil by 1:1 ratio complex, will be better integrated smooth, soft, fluffy results.

Keywords：special smooth silicone oil; ultra-high molecular weight hydroxy silicone oil; amino silicone oil

目  录
中文摘要 I
英文摘要 II
目录 III
1. 绪论 1
 1.1  有机硅及其工业简介 1
 1.2  氨基硅油和羟基硅油 3
 1.2.1  氨基硅油的合成 3
 1.2.2  羟基硅油的合成 4
 1.3  课题的提出及研究内容 6
2. 实验部分 7
 2.1  主要原料和试剂 7
 2.2  主要仪器和设备 7
 2.3  实验步骤 7
 2.4  样品测试 8
      2.4.1  手感测定 8
      2.4.2  分子量的测定 8
3. 结果与讨论 9
 3.1  不锈钢反映釜的设计与建造 9
 3.2  超高分子量硅油的合成 9
      3.2.1 水对分子量的影响 9
      3.2.2 催化剂对分子量的影响 10
      3.2.3 聚合温度对分子量的影响 10
      3.2.4 聚合单体对分子量的影响 11
 3.3  氨基硅油的合成及特滑硅油的配制 11
 3.3.1 氨基硅油的合成 11
 3.3.2 特滑硅油的配制及性能评价 12
4．总结与展望 14
致谢 15
参考文献 16

相关论文 暂无...